Mechanical Properties and Meso-mechanism of Pisha Sandstone with W-OH Solidified Under Drying-wetting Cycles
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    [目的] 对W-OH砒砂岩固结体干湿循环特性及其细观机理进行研究,为实现W-OH固结改良砒砂岩及其耐久性研究提供科学依据。[方法] 采用W-OH(亲水性聚氨酯材料)对砒砂岩进行固结处理,基于无侧限抗压试验、三轴抗压试验,研究其在干湿循环条件下的力学性能,并结合SEM,EDS和称重法对其干湿循环后样品微观结构、元素和质量损失进行分析,以获得其破坏机理。[结果] W-OH砒砂岩固结体的无侧限抗压强度、弹性模量和黏聚力在1~3次干湿循环后升高;在3~9次干湿循环后,固结体的力学强度降低;9次之后,剩下高黏结力的W-OH胶结体包裹于砒砂岩颗粒表面,力学强度趋于稳定。内摩擦角在1~9次干湿循环后上下波动,9次干湿循环后趋于稳定。采用碳元素分析和质量损失分析相结合的方法对土样中W-OH流失特性进行评价,发现土样在1~9次干湿循环中W-OH胶结体逐渐降低,并在9次干湿循环后达到稳定,这与上述宏观力学变化的规律相似,验证了破坏机理,为判断其长期特性提供理论依据。[结论] 研究表明可将9次干湿循环后达到稳定的W-OH砒砂岩固结体的力学性质作为土体的长期力学特性。

    Abstract:

    The effects of drying-wetting cycles on the mechanical properties and meso-mechanism of the hydrophilic polyurethane material(W-OH) solidified Pisha sandstone were conducted to provide scientific basis for the study of W-OH consolidation amending Pisha sandstone and its durability. W-OH was used to consolidate the Pisha sandstone in this study. Macroscopic mechanical properties of the W-OH solidified Pisha sandstone were tested by unconfined compression experiment and triaxial compression experiment. To obtain the meso-mechanism, SEM, EDS and weighing methods were used to analyze the microstructure, elements, and quality losses of the sample after drying-wetting cycles. The results showed that unconfined compressive strength, elastic modulus, and cohesion of the W-OH solidified Pisha sandstone increased after drying-wetting cycles of 1~3 times. During drying-wetting cycles of 3~9 times, the mechanical strength of the W-OH solidified Pisha sandstone decreased. the rest solidified W-OH with high cohesive forces remained on the surface of the Pisha sandstone particles and the mechanical strength tended to be stable after drying-wetting cycles 9 times. The internal friction angle varied with fluctuation from 1 to 9 time drying-wetting cycles and stabilized after 9 times. The W-OH loss in the solidified soil samples was evaluated by the carbon element analysis and mass loss analysis. The solidified W-OH gradually decreased during drying-wetting cycles of 1~9 times and became stable after 9 times, which proved meso-mechanism of macroscopic mechanical properties above-mentioned and provided theoretical basis for long-term characteristics of W-OH consolidated Pisha sandstone. The results of this study suggest that the mechanical properties of W-OH solidified Pisha sandstone after 9 drying-wetting cycles can be considered as the long-term mechanical properties of this material.

    参考文献
    相似文献
    引证文献
引用本文

马雯波,丁哲,吴智仁,梁止水,杨才千. W-OH砒砂岩固结体干湿循环特性及其细观机理[J].水土保持通报,2018,38(6):22-28,34

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-05-22
  • 最后修改日期:2018-06-21
  • 录用日期:
  • 在线发布日期: 2019-01-07
  • 出版日期: